Precimid1174 Pro CF
Precimid1174 Pro CF | Carbon Fiber Reinforced PA12 Powder (Ash Black)
Precimid1174 Pro CF is a PA12 powder with 30% carbon fiber reinforcement for SLS 3D printing. It combines low weight with very high strength and stiffness and stays dimensionally stable at elevated temperatures – ideal for highly loaded lightweight parts.
- 30% carbon fiber: Excellent strength-to-weight ratio.
- High stiffness: Flexural modulus up to 6,000 MPa and tensile modulus up to 9,000 MPa (X direction).
- Heat resistant: Heat deflection temperature of 172 °C, even at 1.82 MPa.
- Wear resistant: For parts under friction and mechanical load.
Specifications Precimid1174 Pro CF
| Property | Test method | X | Y | Z | Unit |
|---|---|---|---|---|---|
| Color | visual | ash black | ash black | ash black | – |
| Density | DIN 53466 | 1.09 | 1.09 | 1.09 | g/cm³ |
| Elongation at break | ASTM D638 | 8.0 | 9.5 | 1.7 | % |
| Flexural strength | ASTM D790 | 135 | 100 | 66 | MPa |
| Flexural modulus | ASTM D790 | 6,000 | 4,500 | 3,000 | MPa |
| Heat deflection temperature (HDT) at 0.45 MPa | ASTM D648 | 172 | 172 | 172 | °C |
| Heat deflection temperature (HDT) at 1.82 MPa | ASTM D648 | 172 | 172 | 172 | °C |
| Tensile strength | ASTM D638 | 88 | 63 | 36 | MPa |
| Tensile modulus | ASTM D638 | 9,000 | 6,400 | 3,500 | MPa |
| Izod impact strength, notched | ASTM D256 | 35 | 35 | 22 | J/m |
| Izod impact strength, unnotched | ASTM D256 | 6.3 | 6.8 | 3.5 | J/m |
| Surface resistance (typical) | IEC 62631-3-2 | 5 | – | 5 | kΩ |
Applications
Precimid1174 Pro CF excels wherever lightweight design and stiffness count:
- Drones
- High-stiffness structural parts
- Parts exposed to heat and pressure
- Robotics
- Automotive
- Aerospace
Compatible SLS Systems
Precimid1174 Pro CF is developed for TPM3D SLS systems and delivers consistent surface quality and mechanical properties – from single parts to series production.